Carbon Black

Carbon Black C65 til lithium-ion batteri råmateriale

 

 

EJENDOM	TESTMETODE(*)	ENHED	GRÆNSER	VÆRDI
Tæthed (i posen)	Intern metode 26	kg/m2	160±20	160
Absorptionsstivhedsværdi	Intern metode 1	ml/5 g	32.0±2.0	33.0
HCI Absorptionsværdi	JIS K1469-1984	ml/5 g	min 16.0	20.8
Korn 45μm/325 mesh	ASTM D1514	ppm	maks. 5.0	＜2
Korn 20μm	ASTM D1514	ppm	max 25	＜7
BET overfladeareal	ASTM D3037-89	m2/g	62.0±5.0	61.2
Fugtindhold (som pakket)	ASTM D1509	%	maks. 0.3	0.1
Total svovl	ASTM D1619	%	maks. 0.030	0.023
Flygtigt stof	Intern metode 2	%	maks. 0.15	0.14
Askeindhold	ASTM D1506	%	maks. 0.025	0.010
Jernindhold	Intern metode 20	ppm	maks. 7.0	1.5
Nikkelindhold	Intern metode 20	ppm		0.1
Vanadium indhold	Intern metode 20	ppm		＜0.5
Toluenekstrakt	ASTM D4527	%	maks. 0.10	＜0.10
Specifik modstand 50 kg/cm2	Intern metode 7	Ohm-cm	maks. 0.25	0.17
Specifik modstand 50 kg/cm2	Intern metode 7	Ohm-cm	maks. 0.15	0.12
Kulstofindhold	Intern metode 27	%	min 99,5	＞99.5
PH	ASTMD1512		8-11.0	9.3

 

Carbon black er et almindeligt anvendt fyldstof ved fremstilling af gummi- og plastprodukter. Den fås i forskellige kvaliteter og typer afhængigt af dens egenskaber og anvendelser. En sådan kvalitet er den elektrisk ledende carbon black C65, som i vid udstrækning bruges til at forbedre den elektriske ledningsevne af forskellige industriprodukter.

 

Ejendomme:
C65 carbon black udviser god elektrisk ledningsevne på grund af tilstedeværelsen af ​​høje niveauer af grafitisk carbon i sin struktur. Den har et højt overfladeareal og lav partikelstørrelsesfordeling, hvilket reducerer modstanden mellem partikler og derved øger ledningsevnen. Det er også meget stabilt og modstandsdygtigt over for nedbrydning, hvilket gør det til et ideelt valg til applikationer, hvor langtidsstabilitet er påkrævet.

 

 

 

 